COMPRESSION PACKING

Compression Packing

General Service Packings

Style 528 Flax - Tallow

Flax
Compression Packing Flax fiber packing lubricated with tallow and wax. Used for brine, cold water and oil service. Ideal for marine applications.
  • Temperature: 220ºF
  • pH: 5-9
  • Speed: 1200 FPM
  • Pressure: To 150 PSI
  • Construction: Square Plaited

Style 531 Flax - Petroleum

Flax - Petroleum
Compression Packing A flax fiber packing, treated with a petroleum-based lubricant and surface graphited.
  • Temperature: 220ºF
  • pH: 5-9
  • Speed: 1200 FPM
  • Pressure: To 150 PSI
  • Construction: Square Braid

Style 1398 Syntex

Syntex
Compression Packing This syntex fiber packing is thoroughly impregnated with a high temperature lubricant. The finished packing is surface graphited. This packing is an asbestos replacement packing for general service use on pumps and valves.
  • Temperature: To 500ºF
  • pH: 4-10
  • Speed: 1500 FPM
  • Pressure: To 300 PSI
  • Construction: Interlock Braid
Available with a Moly Lubricant - Style 1398 MOLY

Style 1430 Syntex

Syntex
Compression Packing A syntex fiber packing treated with a high temperature lubricant and graphited. This packing is soft and pliable for general service on pumps and valves.
  • Temperature: To 500ºF
  • pH: 4-10
  • Speed: 1500 FPM
  • Pressure: To 300 PSI
  • Construction: Square Braid
Available with a Moly Lubricant - Style 1430 MOLY

PTFE & PTFE Impregnated Packings

Style 154 Pure PTFE

Pure PTFE
Compression Packing A PTFE packing, with PTFE dispersion. It is a dense, firm packing used in valve and slow speed pump applications. This packing has excellent chemical resistance.
  • Temperature: To 500ºF
  • pH: 0-14
  • Speed: 1000FPM
  • Pressure: Pumps: 300 PSI;
    Valves: 2000 PSI
  • Construction: Interlock Braid

Style 154S Pure PTFE

Pure PTFE
Compression Packing A PTFE packing treated with an inert lubricant. This is a soft and resilient packing for chemical pump and valve applications.
  • Temperature: To 500ºF
  • pH: 0-14
  • Speed: 1500 FPM
  • Pressure: Pumps: To 300 PSI
  • Construction: Interlock Braid

Style 154 FDA Pure PTFE

Pure PTFE
Compression Packing A food Grade FDA PTFE filament packing, that is food grade, constructed in an interlock braid with an FDA break-in lube.
  • Temperature: To 500ºF
  • pH: 0-14
  • Speed: 1500 FPM
  • Pressure: Pumps: 300 PSI; Valves: 2000 PSI
  • Construction: Interlock Braid
Braided PTFE tape - Style 156

Style 182 PTFE Impregnated Aramid

PTFE - Aramid
Compression Packing A spun aramid fiber with each strand impregnated with PTFE dispersion prior to and after braiding, it also has break-in lubricant. This packing is ideal for valves and pumps in abrasive service.
  • Temperature: To 500ºF
  • pH: 2-12
  • Speed: 2250 FPM
  • Pressure: 500 PSI
  • Construction: Interlock Braid

Style 525T Flax - PTFE

Flax - PTFE
Compression Packing A premier marine service packing made with flax fibers and lubricated with PTFE dispersion. This packing has low friction and high tensile strength. It is excellent for water service, paper mill applications and marine stern tube & rudder posts.
  • Temperature: 250ºF
  • pH: 4-9
  • Speed: 1500 FPM
  • Pressure: To 200 PSI
  • Construction: Square Braid

Style 1152 PTFE Impregnated Syntex

PTFE - Syntex
Compression Packing A special syntex fiber packing, with each strand impregnated with a PTFE dispersion. The finished packing also has a break-in lubricant. It is an asbestos replacement packing for general service applications. This packing has good chemical resistance.
  • Temperature: To 500ºF
  • pH: 0-12
  • Speed: 2200 FPM
  • Pressure: to 500 PSI
  • Construction: Interlock Braid

Style 1152K PTFE Impregnated Syntex with Kevlar Corners

PTFE - Syntex with Kevlar Corners
Compression Packing A unique packing combining 1152 and 170 fibers. The aramid corners prevent roll and extrusion. This packing is well suited for abrasive applications and end rings with other packings.
  • Temperature: To 500ºF
  • pH: 3-12
  • Speed: 2200 FPM
  • Pressure: to 500 PSI
  • Construction: Interlock Braid

Carbon and Graphite Packings

Style 50 Carbon Yarn with PTFE

Carbon Yarn with PTFE
Compression Packing A carbon yarn packing heavily impregnated with PTFE dispersion. This packing is for severe services in pumps or valves handling chemicals, solvents and acids. It is an ideal packing for paper mill applications.
  • Temperature: To 600ºF
  • pH: 0-14
  • Speed: 3000 FPM
  • Pressure: To 500 PSI
  • Construction: Interlock Braid

Style 90 Carbon Yarn with Graphite

Carbon - Graphite
Compression Packing A carbon yarn packing impregnated with graphite dispersion. This packing is for severe services in pump and valve applications, including super-heated steam, acids, alkalis, etc.
  • Temperature: Atmosphere: 850ºF
    Steam: 1200ºF
  • pH: 0-14
  • Speed: 4000 FPM
  • Pressure: Pumps: 500 PSI;
    Valves: 2500 PSI
  • Construction: Interlock Braid

Style 160 Graphite Filament

Graphite - Graphite
Compression Packing A graphite filament packing impregnated with a graphite dispersion. This packing is recommended for severe service applications where leakage must be held to a minimum. It has excellent chemical resistance.
  • Temperature: Atmosphere: 850ºF; Steam: 1200ºF
  • pH: 0-14
  • Speed: 4000 FPM
  • Pressure: Pumps: 500 PSI; Valves: 2500 PSI
  • Construction: Interlock Braid

Style 165 GFO

GFO - Graphite Filled PTFE
Compression Packing A graphite filled PTFE fiber packing that improves thermal conductivity and will not harden. This packing is commonly called GFO®. It has excellent chemical resistance.
  • Temperature: To 550ºF
  • pH: 0-14
  • Speed: 4300 FPM
  • Pressure: 300 PSI
  • Construction: Interlock Braid

Style 165K GFO with Kevlar Corners

GFO - Kevlar Corners
Compression Packing A unique aramid packing combining styles 165 and 170 fibers. This packing has aramid corners that prevent roll and extrusion. It is an excellent service packing in severe pump applications. This packing is widely used in paper mills.
  • Temperature: To 550ºF
  • pH: 2-12
  • Speed: 2500 FPM
  • Pressure: 300 PSI
  • Construction: Interlock Braid

Style 3165

GFO - PTFE
Compression Packing A packing made from a special blend of PTFE and graphite fibers plus a high temperature lubricant. It is an economical substitute for style 165. It is a good chemical and abrasion resistant packing.
  • Temperature: To 550ºF
  • pH: 0-14
  • Speed: 4500 FPM
  • Pressure: 300 PSI
  • Construction: Interlock Braid


Aramid, Valve Stem & Fiberglass Packings

Style 170 Aramid Fiber

Aramid Fiber
Compression Packing This is an aramid fiber packing with an inert lubricant. It is an extremely durable, highly abrasive resistant packing. This packing is ideal for slurry service.
  • Temperature: To 500ºF
  • pH: 3-11
  • Speed: 1900 FPM
  • Pressure: 500 PSI
  • Construction: Interlock Braid

Style 182 Aramid Fiber with PTFE

Aramid Fiber with PTFE
Compression Packing This is a spun aramid fiber packing with a PTFE dispersion and a break-in lubricant. It is ideal for valves and pumps in abrasive service.
  • Temperature: To 500ºF
  • pH: 2-12
  • Speed: 2250 FPM
  • Pressure: 500 PSI
  • Construction: Interlock Braid

Style 1100TCP Valve Stem Packing

Pure Graphite
Compression Packing A packing braided from pure expanded graphite. It is resilient, self-lubricating, chemically inert and thermally conductive. 1100TCP can be used in both pumps and valves in a wide range of service conditions.
  • Temperature: Steam: 1200ºF; Atmosphere: 850ºF
  • pH: 0-14 except strong oxidizers
  • Speed: 4000 FPM
  • Pressure: 3000 PSI
  • Construction: Interlock Braid

Style 1414 Valve Stem Packing

Carbon with Inconel Wire
Compression Packing A high temperature packing made from carbon yarn with an inconel wire braided over a resilient core, thoroughly impregnated with graphite and corrosion inhibitor. It has excellent chemical resistance.
  • Temperature: To 1200ºF - Steam
  • pH: 1-12
  • Pressure: 2500 PSI
  • Construction: Braid over Core

Style 1416 Dry Fiberglass Packing

Dry Fiberglass
Compression Packing This is a texturized fiberglass fiber packing. It is braided dry with no lubricant. This packing will not swell, shrink and is completely incombustible. It is used for sealing oven doors. It has excellent chemical resistance.
  • Temperature: To 1000ºF
  • pH: 2-11
  • Construction: Square Braid

Packing Construction

Square Square Interlock Interlock Braid over Core Braid over Core
Square Braid Interlocked Braid Braid over Core

line

GO TO TABLE OF CONTENTS

GO TO MAIN PAGE

line

Tampa Rubber & Gasket Co., Inc.

215 North 20th Street
Tampa, FL, USA 33605
Ph-813-247-3647 Fax-813-247-3180
Toll Free-800-940-4673 E-Mail - The Post Office
Visa Mastercard
American Express Discover
We accept Visa, Mastercard, American Express & Discover


Validated!
click here

w3c Validated
COPYRIGHT © 1998-2004 TAMPA RUBBER & GASKET CO., INC.